Alloy | Tensile Strength | Yield Strength (0.2%) | Impact Strength | Macro (apparent) | Macro (apparent) | Micro-Indentation (converted) | Young's Modulus | Poisson's Ratio | Elongation | |
PSI x 10³ | PSI x 10³ | ft lb | HRB | HRC | Rockwell | Gpa | Ratio | % in 25.4mm | ||
| 4140 Q&T High Hardness | 260 | 215 | 36 | - | 55 | 56 | - | 0.28 | 7 | |
|---|---|---|---|---|---|---|---|---|---|---|
| 4140 Q&T Low Hardness | 160 | 145 | 71 | - | 35 | 31 | - | 0.28 | 13 | |
| MIM-316L | 75 | 25 | 140 | 67 | - | - | 190 | 0.28 | 50 | |
| MIM-4605 (as sintered) | 64 | 30 | 50 | 62 | - | - | 200 | 0.28 | 15 | |
| MIM-Cu (Copper) | 24 | 21 | - | - | - | - | - | - | 30 | |
| S7 (HIP) | 310 | 250 | - | - | 60 | 60 | - | - | 4.5 | |
| S7 (No HIP) | 190 | 170 | - | - | 51 | 60 | - | - | 1 | |
| MIM F75 (ASTM F75) - Hipped | 147 | 81 | 130 | - | 25 | - | - | - | 30 | |
| MIM-420 (HIP and vacuum heat treated) | 252 | 186 | 61 | - | 45 | - | - | - | 3.5 | |
| MIM-4605 (quenched & tempered | 265 | 230 | 40 | - | 58 | 60 | 205 | 0.28 | 3 | |
| high hardness) | 265 | 230 | 40 | - | 58 | 60 | 205 | 0.28 | 3 | |
| MIM-440C (HIP and heat treated) | 250 | 235 | 85 | - | 54 | - | - | - | 1.8 | |
| MIM-4605 (quenched and tempered | 195 | 182 | 28 | - | 40 | 47 | - | - | 9 | |
| low hardness) | 195 | 182 | 28 | - | 40 | 47 | - | - | 9 | |
| MIM-F-15 (as sintered) | 67 | 43 | - | 65 | - | - | - | - | 25 | |
| MIM-17-4 PH (as sintered) | 130 | 106 | 100 | - | 27 | 25 | 190 | 0.29 | 6 | |
| MIM-F1537 – ASTM F1537 (HIP and heat treated) | 160 | 12 | 59 | - | 32 | - | - | - | 27 | |
| MIM-17-4 PH (heat treated) | 172 | 158 | 100 | - | 33 | 40 | 190 | 0.29 | 10 | |
| MIM-17-4 H900 | 175 | 160 | - | - | 40 | 40 | - | - | 10 | |
| MIM-17-4 H1100 | 145 | 132 | - | - | 34 | - | - | - | 12 | |
| MIM-K1 (as sintered) | 74 | - | - | 98 | - | - | - | - | 1.5 | |
| MIM-K3 (heat treated) | 250 | 230 | 30 | - | 58 | 58 | - | - | 4 | |
| 420Nb | ||||||||||
| 4602 | 60 | 46 | ||||||||
| 8620 | 56 | |||||||||
| FN0205 (heat treated) | 174 | 145 | 55 | 2 | ||||||
| Nitronic 60 | 91 | 48 | 18 | |||||||
| T400 | ||||||||||
| 50Ni50Fe | 66 | 23 | 50 | 30 | ||||||
| 12-Cr | 54 | 29.5 | 230 | 83 | 30 | |||||
| FeSi-2 | 70 | 48.5 | 157 | 81.5 | 24 |