다이나믹 프로세스 & 메탈 셀렉터

Imperial US/UK

Metric

FILTERS

Clear All Filters

Tensile Strength (PSI x 10³)

0 PSI x 10³

>0 PSI x 10³

60 PSI x 10³

Yield Strength (0.2%) (PSI x 10³)

0 PSI x 10³

>0 PSI x 10³

60 PSI x 10³

Elongation (% in 50mm)

0% in 50mm

>0% in 50mm

15 % in 50mm

4140 Q&T High Hardness	260	215	36	-	55	56	-	0.28	7
Alloy	Tensile Strength	Yield Strength (0.2%)	Impact Strength	Macro (apparent)	Macro (apparent)	Micro-Indentation (converted)	Young's Modulus	Poisson's Ratio	Elongation
	PSI x 10³	PSI x 10³	ft lb	HRB	HRC	Rockwell	Gpa	Ratio	% in 25.4mm
4140 Q&T Low Hardness	160	145	71	-	35	31	-	0.28	13
MIM-316L	75	25	140	67	-	-	190	0.28	50
MIM-4605 (as sintered)	64	30	50	62	-	-	200	0.28	15
MIM-Cu (Copper)	24	21	-	-	-	-	-	-	30
S7 (HIP)	310	250	-	-	60	60	-	-	4.5
S7 (No HIP)	190	170	-	-	51	60	-	-	1
MIM F75 (ASTM F75) - Hipped	147	81	130	-	25	-	-	-	30
MIM-420 (HIP and vacuum heat treated)	252	186	61	-	45	-	-	-	3.5
MIM-4605 (quenched & tempered	265	230	40	-	58	60	205	0.28	3
high hardness)	265	230	40	-	58	60	205	0.28	3
MIM-440C (HIP and heat treated)	250	235	85	-	54	-	-	-	1.8
MIM-4605 (quenched and tempered	195	182	28	-	40	47	-	-	9
low hardness)	195	182	28	-	40	47	-	-	9
MIM-F-15 (as sintered)	67	43	-	65	-	-	-	-	25
MIM-17-4 PH (as sintered)	130	106	100	-	27	25	190	0.29	6
MIM-F1537 – ASTM F1537 (HIP and heat treated)	160	12	59	-	32	-	-	-	27
MIM-17-4 PH (heat treated)	172	158	100	-	33	40	190	0.29	10
MIM-17-4 H900	175	160	-	-	40	40	-	-	10
MIM-17-4 H1100	145	132	-	-	34	-	-	-	12
MIM-K1 (as sintered)	74	-	-	98	-	-	-	-	1.5
MIM-K3 (heat treated)	250	230	30	-	58	58	-	-	4
420Nb
4602					60	46
8620					56
FN0205 (heat treated)	174	145			55				2
Nitronic 60	91	48							18
T400
50Ni50Fe	66	23		50					30
12-Cr	54	29.5	230	83					30
FeSi-2	70	48.5	157	81.5					24

** For comparison only.